Name: SnapSpeed PLA Filament (RFID) - 1KG
Brand: Snapmaker
SKU: 34071
Price: 19.99 USD
Availability: OutOfStock
Rating: 4.9 (9 reviews)

1 88

SnapSpeed PLA Filament (RFID) - 1KG

Snapmaker SnapSpeed PLA

High Speed

Stable Performance

Easy Print

Snapmaker SnapSpeed PLA

Snapmaker SnapSpeed PLA Filament spools with a winter cabin 3D print, highlighting high-speed, stable, easy-print PLA filament.

High Speed, High Stability

Optimized fluid dynamics enable speeds up to 300mm/s while ensuring smooth, high-quality prints.

Optimized Layer Adhesion

Strong layer adhesion ensures firm bonding and flawless prints, even at high speeds.

Smoother Prints, Finer Finish

SnapSpeed PLA ensures smooth extrusion and optimized cooling for sleek,
detailed prints with a refined finish, even at high speeds.

Tougher Than Ever

Engineered for durability and strength. Perfect for functional parts and prototypes.
Resilient in the face of everyday use.

Precision at High Speeds

Bubble-free vacuum spools feed flawlessly. Anti-clog heat control eliminates jams and flow breaks. Tangle-to-tip precision.

Sustainably Made, Responsibly Used

SnapSpeed PLA is made from 100% renewable plant-based resources and packaged with fully biodegradable cardboard spools, offering a safer choice for both users and the environment.

Specifications

RECOMMENDED PRINTING CONDITIONS5

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature

Classic: 190–210 °C
High-speed: 210–230 °C

Build plate temperature

25–60 °C

Build surface treatment

Glue when needed

Printing speed

Classic: 50-100mm/s
High-speed: 100-300mm/s

Drying setting

55°C for 6h

PHYSICAL PROPERTIES

Density

1.23g/cm³ at 21.5°C

Melt index

15.4 g/10min

THERMAL PROPERTIES

Glass transition temperature

59°C

Melting temperature

164°C

Crystallization temperature

96°C

Decomposition temperature

370°C

Vicat softening temperature

61°C

Heat deflection temperature (ISO 75 1.8MPa)

52°C

Heat deflection temperature (ISO 75 0.45MPa)

53°C

MECHANICAL PROPERTIES - Classic Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. Classic prirhting speed = 46.7mm/s, printing temperature = 210 °C

Young's modulus (X-Y)

2878.3±74.3 MPa

Young's modulus (Z)

2689.8±92.0 MPa

Tensile strength (X-Y)

46.0±0.5 MPa

Tensile strength (Z)

37.3±0.7 MPa

Elongation at break

21.5±5.02%

Elongation at break (Z)

4.2±2.0%

Bending modulus (X-Y)

2868.2±78.4 MPa

Bending strength (X-Y)

76.5±0.9 MPa

Charpy impact strength (X-Y)

6.1±0.6 kJ/m²

MECHANICAL PROPERTIES - High Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. High printing speed = 300mm/s, printing temperature = 230 °C

Young's modulus (X-Y)

2649.7±78.3 MPa

Young's modulus (Z)

2433.4±79.4 MPa

Tensile strength (X-Y)

43.9±0.4 MPa

Tensile strength (Z)

32.4±0.4 MPa

Elongation at break

15.1±3.9%

Elongation at break (Z)

3.3±0.5%

Bending modulus (X-Y)

2797.9±40.7 MPa

Bending strength (X-Y)

71.4±0.6 MPa

Charpy impact strength (X-Y)

5.0±0.5 kJ/m²

RECOMMENDED PRINTING CONDITIONS

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature

Classic: 190–210 °C
High-speed: 210–230 °C

Build plate temperature

25–60 °C

Build surface treatment

Glue when needed

Printing speed

Classic: 50-100mm/s
High-speed: 100-300mm/s

Drying setting

55°C for 6h

PHYSICAL PROPERTIES

Density

1.23g/cm³ at 21.5°C

Melt index

15.4 g/10min

THERMAL PROPERTIES

Glass transition temperature

59°C

Melting temperature

164°C

Crystallization temperature

96°C

Decomposition temperature

370°C

Vicat softening temperature

61°C

Heat deflection temperature (ISO 75 1.8MPa)

52°C

Heat deflection temperature (ISO 75 0.45MPa)

53°C

MECHANICAL PROPERTIES - Classic Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. Classic prirhting speed = 46.7mm/s, printing temperature = 210 °C

Young's modulus (X-Y)

2878.3±74.3 MPa

Young's modulus (Z)

2689.8±92.0 MPa

Tensile strength (X-Y)

46.0±0.5 MPa

Tensile strength (Z)

37.3±0.7 MPa

Elongation at break

21.5±5.02%

Elongation at break (Z)

4.2±2.0%

Bending modulus (X-Y)

2868.2±78.4 MPa

Bending strength (X-Y)

76.5±0.9 MPa

Charpy impact strength (X-Y)

6.1±0.6 kJ/m²

MECHANICAL PROPERTIES - High Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. High printing speed = 300mm/s, printing temperature = 230 °C

Young's modulus (X-Y)

2649.7±78.3 MPa

Young's modulus (Z)

2433.4±79.4 MPa

Tensile strength (X-Y)

43.9±0.4 MPa

Tensile strength (Z)

32.4±0.4 MPa

Elongation at break

15.1±3.9%

Elongation at break (Z)

3.3±0.5%

Bending modulus (X-Y)

2797.9±40.7 MPa

Bending strength (X-Y)

71.4±0.6 MPa

Charpy impact strength (X-Y)

5.0±0.5 kJ/m²

SnapSpeed PLA Filament (RFID) - 1KG

Featured RFID Filament

Matte PLA Filament (RFID) - 1KG

Basic PLA Filament (1kg)

Black Nylon Filament (1kg)

PVA Filament (500g)

Fast Local Shipping

1-Year Warranty

Easy Returns

30-Day Price Match

Snapmaker SnapSpeed PLA

Snapmaker SnapSpeed PLA

High Speed, High Stability

Optimized Layer Adhesion

Smoother Prints, Finer Finish

Tougher Than Ever

Precision at High Speeds

Sustainably Made, Responsibly Used

Specifications