Subscribe to get updates on our new products and exclusive promotions.
Product Overview
• High-speed printing up to 300 mm/s.
• Superior toughness and structural strength for functional parts.
• Enhanced resistance to heat and moisture.
• Durable performance in both indoor and outdoor settings.
• Exclusive RFID auto-loading for Snapmaker U1.
Applicability
• 3D Printing
Compatibility:
• Snapmaker U1: Optimized profiles built into Snapmaker Orca.
• Other printers: Supports most FDM 3D printers; manual tuning may be required.
Recommendations
2+ rolls: $18.40/roll | 4+ rolls: $16.10/roll | 6+ rolls: $14.95/roll | 10+ rolls: $13.11/roll
2+ rolls: $18.40/roll | 4+ rolls: $16.10/roll | 6+ rolls: $14.95/roll | 10+ rolls: $13.11/roll
Payment Methods
Delivery
• 48 states, AK, HI: Ships from U.S. warehouse · 1–2 business days dispatch · 2–7 business days delivery after dispatch
• AE, AP, GU, PR: Ships from U.S. warehouse · 1–2 business days dispatch · 15–30 business days delivery after dispatch
Covers for machines and modules, excluding limited warranty items and consumable parts.
14-Day Returns & Eligible Refunds.
Get the price difference as a Gift Card if the price drops within 30 days.
Designed for print speeds of up to 300 mm/s, Snapmaker PETG HF boosts printing efficiency by shortening print time without compromising print quality.
Snapmaker PETG HF offers a reliable combination of toughness and strength, making it a practical choice for durable everyday prints such as hooks, holders, and fixtures.
Enhanced resistance to heat, water, and chemicals compared to regular PETG and PLA. Ideal for durable models that need to withstand the elements, keeping their shape and toughness whether displayed indoors or exposed to sun and rain outdoors.
Engineered for clean lines and sharp details, even when printed at top speeds, Snapmaker PETG HF ensures a consistent, reliable stream, preventing gaps or thin spots.From essential neutrals to vibrant accents, Snapmaker PETG HF offers a curated color spectrum to cover your everyday projects.
From essential neutrals to vibrant accents, Snapmaker PETG HF offers a curated color spectrum to cover your everyday projects.
When used with the Snapmaker U1, the printer automatically loads preset filament information so you don’t need to adjust settings manually, making printing easier than ever.
Both filament and spool are crafted from 100% recyclable materials, balancing eco-friendly values with superior print reliability.
1. Drying & Storage
• Pre-Dry: This filament is pre-dried and vacuum-sealed for immediate use upon opening. However, PETG is sensitive to moisture; if left exposed for a long time, we recommend drying it at 65°C for 6 hours before printing to ensure the best results.
• Re-Dry: If the filament has been left out for a while, always re-dry it before use.
• Storage: Once unboxed, it is best to keep the filament in a sealed container with desiccant.
2. Printing
• Moisture Control: Due to its high hygroscopicity, we recommend printing PETG directly from a sealed container with desiccant to ensure optimal quality. If exposed to air for a long time, print quality may significantly degrade. If you hear popping or crackling sounds during extrusion, the filament must be dried.
• If a Sealed Container with Desiccant Is Unavailable: Consider shortening the print time by reducing the overall model size, lowering the infill density, or increasing the layer height to minimize moisture exposure.
• Cooling & Adhesion: Print with the cooling fan turned off or at a very low speed. Rapid cooling can significantly weaken layer adhesion in PETG. If you still encounter adhesion issues while the fan is off, try increasing the printing temperature.
• Flow Rate: For optimal performance, we recommend a maximum volumetric speed of 15 mm³/s.
Recommended Printing Conditions5
*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.
Nozzle temperature
190–240°C
Bed Temperature
25–70°C
Cooling Fan
ON
Printing speed
Up to 250 mm/s
Preset Printing Speed
119 mm/s
Drying Settings Before Printing
55°C for 6 h
Physical Properties
Density
1.24 g/cm³ (23°C)
Melt index
21.17 g/10 min (210°C, 2.16 kg)
Melting Temperature
162.3°C (DSC, 10°C/min)
Glass Transition Temperature
58.2°C (DSC, 10°C/min)
Vicar Softening Temperature
64.7°C
Saturated Water Absorption Rate
0.45% (23°C, 70% RH)
Mechanical Properties
Tensile Strength (X-Y)
41.1 ± 0.8 MPa
Tensile Strength (Z)
23.8 ± 2.8 MPa
Breaking Elongation Rate (X-Y)
> 40%
Breaking Elongation Rate (Z)
1.2 ± 0.16%
Bending Modulus (X-Y)
2241.4 ± 140.4 MPa
Bending Modulus (Z)
2063.5 ± 95.9 MPa
Bending Strength (X-Y)
69.1 ± 1.6 MPa
Bending Strength (Z)
37.3 ± 5.5 MPa
Impact Strength (X-Y)
13.8 ± 1.3 kJ/m²
Impact Strength (Z)
11.2 ± 0.9 kJ/m²
Recommended Printing Conditions
*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.
Nozzle temperature
240–260°C
Bed Temperature
60–80°C
Cooling Fan
20%–40%
Printing speed
Up to 300 mm/s
Drying Settings
65°C for 6 h
Physical Properties
Density
1.30 g/cm³ (23°C)
Melt index
16.3 g/10 min (230°C, 2.16 kg)
Glass Transition Temperature
71.24°C (DSC, 10°C/min)
Vicat Softening Temperature
75°C
Saturated Water Absorption Rate
0.51% (70% RH, 23°C)
Mechanical Properties
Tensile Strength (X-Y)
47.96 ± 4.88 MPa
Tensile Strength (Z)
45.71 ± 1.76 MPa
Breaking Elongation Rate (X-Y)
9.33 ± 6.57%
Breaking Elongation Rate (Z)
3.54 ± 2.35%
Bending Modulus (X-Y)
2277.34 ± 198.09 MPa
Bending Modulus (Z)
1958.74 ± 126.39 MPa
Bending Strength (X-Y)
80.08 ± 3.53 MPa
Bending Strength (Z)
57.65 ± 5.63 MPa
Impact Strength (X-Y)
4.95 ± 0.55 kJ/m² (Notched)
20.24 ± 3.95 kJ/m²
Impact Strength (Z)
15.74 ± 3.91 kJ/m²
Recommended Printing Conditions
* Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters.
Nozzle Temperature
240–260°C
Bed Temperature
60–80°C
Cooling Fan
20%–40%
Printing Speed
Up to 300 mm/s
Drying Setting
65°C for 6h
Physical Properties
Density
1.30 g/cm³ (23°C)
Melt Index
16.3 g/10 min (230°C, 2.16 kg)
Glass Transition Temperature
71.24°C (DSC, 10°C/min)
Vicat Softening Temperature
75°C
Saturated Water Absorption Rate
0.51% (70% RH, 23°C)
Mechanical Properties
Tensile Strength (X-Y)
47.96 ± 4.88 MPa
Tensile Strength (Z)
45.71 ± 1.76 MPa
Breaking Elongation Rate (X-Y)
9.33 ± 6.57%
Breaking Elongation Rate (Z)
3.54 ± 2.35%
Bending Modulus (X-Y)
2277.34 ± 198.09 MPa
Bending Modulus (Z)
1958.74 ± 126.39 MPa
Bending Strength (X-Y)
80.08 ± 3.53 MPa
Bending Strength (Z)
57.65 ± 5.63 MPa
Impact Strength (X-Y)
4.95 ± 0.55 kJ/m² (Notched)
20.24 ± 3.95 kJ/m²
Impact Strength (Z)
15.74 ± 3.91 kJ/m²
Sealed Spool Filament × 1
Desiccant × 1
Paper Packaging Box × 1
Sealed Spool Filament × 1
Desiccant × 1
Paper Packaging Box × 1
Note:
[1] Actual print speeds may vary depending on model complexity and settings. Model Dimensions: 135 × 129 × 200 mm³; Printer: Snapmaker U1; Nozzle Diameter: 0.4 mm; Nozzle Temperature: 245 °C; Layer Height: 0.2 mm; Infill Density: 15%
[2] RFID function is only available for the Snapmaker U1.
Frequently Asked Questions
| Build Plate | Compatibility |
| U1 Textured PEI Steel Plate | Compatible |
| U1 Smooth PEI Steel Plate | Compatible, Clue is required for proper bed adhesion and reliable printing |
| U1 Graphic Effect Steel Plate | Compatible |
| Comparison Dimensions | PETG Basic | PETG HF |
| Flowability | Moderate | Higher |
| Recommended Print Speed | 40–80 mm/s | 100–300 mm/s |
| Surface Quality | Good at low speed, noticeable degradation at high speed | Maintains good quality even at high speed |
| Layer Adhesion | Good | More consistent (significant advantage at high speed) |
| Printing Difficulty | Moderate (requires tuning) | More forgiving and stable |
| Mechanical Properties | Standard PETG strength | Standard PETG strength |
To reduce stringing, you can optimize printing conditions in the following ways:
• Dry the filament thoroughly before use and ensure it remains moisture-free during printing, as moisture is a major cause of stringing
• Slightly reduce the printing temperature to minimize excessive filament oozing
• Slightly increase the retraction distance to better control material flow during travel moves
Product Overview
• High-speed printing up to 300 mm/s.
• Superior toughness and structural strength for functional parts.
• Enhanced resistance to heat and moisture.
• Durable performance in both indoor and outdoor settings.
• Exclusive RFID auto-loading for Snapmaker U1.
Applicability
• 3D Printing
Compatibility:
• Snapmaker U1: Optimized profiles built into Snapmaker Orca.
• Other printers: Supports most FDM 3D printers; manual tuning may be required.
Color
