Product Overview
• Vibrant silk finish with a high-gloss, reflective sheen.
• Stable extrusion and uniform flow for clean surfaces.
• Enhanced interlayer adhesion for improved structural strength.
• Exclusive RFID auto-loading for Snapmaker U1.
• Beginner-friendly and intuitive to use.
Applicability
• 3D Printing
Printer Support & Settings:
• Snapmaker U1: Optimized profiles built into Snapmaker Orca.
• Other printers: Supports most FDM 3D printers; manual tuning may be required.
Recommendations
2+ rolls: $18.40/roll | 4+ rolls: $16.10/roll | 6+ rolls: $14.95/roll | 10+ rolls: $13.11/roll
2+ rolls: $18.40/roll | 4+ rolls: $16.10/roll | 6+ rolls: $14.95/roll | 10+ rolls: $13.11/roll
Payment Methods
Delivery
• 48 states, AK, HI: Ships from U.S. warehouse · 1–2 business days dispatch · 2–7 business days delivery after dispatch
• AE, AP, GU, PR: Ships from U.S. warehouse · 1–2 business days dispatch · 15–30 business days delivery after dispatch
Covers for machines and modules, excluding limited warranty items and consumable parts.
14-Day Returns & Eligible Refunds.
Get the price difference as a Gift Card if the price drops within 30 days.
Snapmaker Silk PLA gives prints a smooth, glossy finish with a refined silk-like sheen. Perfect for decorative models, display pieces, and other designs that deserve a more premium look.
With enhanced interlayer adhesion and improved strength, Snapmaker Silk PLA combines a silky, elegant finish with dependable durability.
The upgraded formula supports stable extrusion and consistent flow for smoother, more reliable printing. From fine details to curved surfaces, it helps deliver clean lines and a polished finish with less hassle.
Available in a range of vivid, eye-catching colors, Snapmaker Silk PLA makes it easy to print with a distinctive visual appeal. From decorative pieces to character models, add style and personality to your creations.
When used with the Snapmaker U1, the printer automatically loads preset filament information so you don’t need to adjust settings manually, making printing easier than ever.
Both filament and spool are crafted from 100% recyclable materials, balancing eco-friendly values with superior print reliability.
1. Drying & Storage
• Pre-Dry: For best results, it is recommended to dry the filament at 55°C for 6 hours before use.
• Re-Dry: After prolonged air exposure, recommend re-drying the filament before starting a print.
• Storage: It's best to keep the filament in a sealed container with desiccant to prevent moisture buildup.
2. Getting the Best Shine
The glossiness of Silk PLA depends on temperature and speed. For a shinier finish, print slower or use a higher temperature.
Recommended Printing Conditions
*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.
Nozzle Temperature
190–240°C
Bed Temperature
25–70°C
Cooling Fan
ON
Printing Speed
Up to 250 mm/s
Drying Settings Before Printing
55°C for 6 h
Physical Properties
Density
1.24 g/cm³ (23°C)
Melt Index
21.17 g/10 min (210°C, 2.16 kg)
Melting Temperature
162.3°C (DSC, 10°C/min)
Glass Transition Temperature
58.2°C (DSC, 10°C/min)
Vicat Softening Temperature
64.7°C
Saturated Water Absorption Rate
0.45% (23°C, 70% RH)
Mechanical Properties
Tensile Strength (X-Y)
41.1 ± 0.8 MPa
Tensile Strength (Z)
23.8 ± 2.8 MPa
Breaking Elongation Rate (X-Y)
> 40%
Breaking Elongation Rate (Z)
1.2 ± 0.16%
Bending Modulus (X-Y)
2241.4 ± 140.4 MPa
Bending Modulus (Z)
2063.5 ± 95.9 MPa
Bending Strength (X-Y)
69.1 ± 1.6 MPa
Bending Strength (Z)
37.3 ± 5.5 MPa
Impact Strength (X-Y)
13.8 ± 1.3 kJ/m²
Impact Strength (Z)
11.2 ± 0.9 kJ/m²
Recommended Printing Conditions
*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.
Nozzle Temperature
190–240°C
Bed Temperature
25–70°C
Cooling Fan
ON
Printing Speed
Up to 250 mm/s
Drying Settings Before Printing
55°C for 6h
Physical Properties
Density
1.24 g/cm³ (23°C)
Melt Index
21.17 g/10 min (210°C, 2.16 kg)
Melting Temperature
162.3°C (DSC, 10°C/min)
Glass Transition Temperature
58.2°C (DSC, 10°C/min)
Vicat Softening Temperature
64.7°C
Saturated Water Absorption Rate
0.45% (23°C, 70% RH)
Mechanical Properties
Tensile Strength (X-Y)
41.1 ± 0.8 MPa
Tensile Strength (Z)
23.8 ± 2.8 MPa
Breaking Elongation Rate (X-Y)
> 40%
Breaking Elongation Rate (Z)
1.2 ± 0.16%
Bending Modulus (X-Y)
2241.4 ± 140.4 MPa
Bending Modulus (Z)
2063.5 ± 95.9 MPa
Bending Strength (X-Y)
69.1 ± 1.6 MPa
Bending Strength (Z)
37.3 ± 5.5 MPa
Impact Strength (X-Y)
13.8 ± 1.3 kJ/m²
Impact Strength (Z)
11.2 ± 0.9 kJ/m²
Sealed Spool Filament × 1
Desiccant × 1
Paper Packaging Box × 1
Sealed Spool Filament × 1
Desiccant × 1 × 1
Paper Packaging Box × 1
Note:
[1] RFID function is only available for the Snapmaker U1.
Frequently Asked Questions
| Build Plate | Compatibility |
| U1 Textured PEI Steel Plate | Compatible |
| U1 Smooth PEI Steel Plate | Compatible |
| U1 Graphic Effect Steel Plate | Compatible |
To reduce stringing, you can optimize printing conditions in the following parameters:
• Lower the printing temperature (key adjustment to reduce oozing)
• Dry the filament thoroughly and ensure it remains moisture-free during use, as moisture is a major cause of stringing
• Slightly increase the retraction distance to better control filament flow during travel moves
Product Overview
• Vibrant silk finish with a high-gloss, reflective sheen.
• Stable extrusion and uniform flow for clean surfaces.
• Enhanced interlayer adhesion for improved structural strength.
• Exclusive RFID auto-loading for Snapmaker U1.
• Beginner-friendly and intuitive to use.
Applicability
• 3D Printing
Printer Support & Settings:
• Snapmaker U1: Optimized profiles built into Snapmaker Orca.
• Other printers: Supports most FDM 3D printers; manual tuning may be required.
Color