PLA Filament (1kg)

Weight:

1 kg

Diameter:

1.75 mm

Length:

330 m / 360.89 "'

Spool Size:

200 × 65 mm / 7.87 × 2.56 "

Printing Temperature:

190 °C - 210 °C

Heated Bed Temperature:

25 °C - 60 °C

Density:

1.24 (g/cm³）

Printing Speed:

user-defined

MFR (g/10 min):

5 (190 ºC/2.16 kg) / (190 ºC/4.76 lbs.)

Tensile strength:

66 / MPa

Elongation at break:

9%

Bending Strength:

98 / MPa

Flexural Modulus:

3640 / MPa

HDT:

60 °C

Weight:

1 kg

Diameter:

1.75 mm

Length:

330 m / 360.89 "'

Spool Size:

200 × 65 mm / 7.87 × 2.56 "

Printing Temperature:

190 °C - 210 °C

Heated Bed Temperature:

25 °C - 60 °C

Density:

1.24 (g/cm²）

Printing Speed:

user-defined

MFR (g/10 min):

5 (190 ºC/2.16 kg) / (190 ºC/4.76 lbs.)

Tensile strength:

66 / MPa

Elongation at break:

9%

Bending Strength:

98 / MPa

Flexural Modulus:

3640 / MPa

HDT:

60 °C

Weight:

1 kg

Diameter:

1.75 mm

Length:

330 m / 360.89 "'

Spool Size:

200 × 65 mm / 7.87 × 2.56 "

Printing Temperature:

190 °C - 210 °C

Heated Bed Temperature:

25 °C - 60 °C

Density:

1.24 (g/cm²）

Printing Speed:

user-defined

MFR (g/10 min):

5 (190 ºC/2.16 kg) / (190 ºC/4.76 lbs.)

Tensile strength:

66 / MPa

Elongation at break:

9%

Bending Strength:

98 / MPa

Flexural Modulus:

3640 / MPa

HDT:

60 °C

Weight:

1 kg

Diameter:

1.75 mm

Length:

330 m / 360.89 "'

Spool Size:

200 × 65 mm / 7.87 × 2.56 "

Printing Temperature:

190 °C - 210 °C

Heated Bed Temperature:

25 °C - 60 °C

Density:

1.24 (g/cm³）

Printing Speed:

user-defined

MFR (g/10 min):

5 (190 ºC/2.16 kg) / (190 ºC/4.76 lbs.)

Tensile strength:

66 / MPa

Elongation at break:

9%

Bending Strength:

98 / MPa

Flexural Modulus:

3640 / MPa

HDT:

60 °C